丁晓宁,王伟宏,张显权.刨花形态和施胶量对玉米秸秆刨花板性能的影响[J].木材科学与技术,2021,35(03):31-37.
DING Xiao-ning,WANG Wei-hong,ZHANG Xian-quan.Effects of Particle Geometry and Resin Content on the Performance of Corn Straw Particleboards[J].Chinese Journal of Wood Science and Technology,2021,35(03):31-37.
以黑龙江省产玉米秸秆为原料，加工6种不同形态的刨花，将刨花形态和施胶量作为两个密切相关的变量进行综合分析，探究制备综合性能良好的玉米秸秆刨花板的工艺方法。结果表明，以筛分粒度24~30目刨花作为芯层、30~40目刨花作为表层制得的三层刨花板性能最佳，静曲强度为32.50 MPa，弹性模量为3.83 GPa，内结合强度为0.93 MPa，24 h吸水厚度膨胀率为14.21%，符合GB/T 4897—2015《刨花板》中干燥状态下使用的重载型刨花板（P4型）的要求。
The corn straws produced in Heilongjiang province were used to prepare particles with six different geometries. The particle geometry and resin content were considered as two closely related variables for the comprehensive analysis to explore the manufacture process of corn straw particleboards aiming to have the excellent comprehensive performance. The experiment results showed with the 24~30,#, particles as the inner layer, and the 30~40,#, particle as the outer layers, a good comprehensive performance could be achieved, i.e., the MOR was up to 32.50 MPa, the MOE was 3.83 GPa, the IB was 0.93 MPa, and the 24 h thickness swelling was 14.21%, which met the requirement of the heavy-duty load bearing particleboard (P4 type) in the national standard of GB/T 4897—2015 ,Particleboard,.
玉米秸秆刨花板刨花形态施胶量动态热机械分析物理力学性能
corn straw particleboardparticle geometryresin contentdynamic thermomechanical analysisphysical and mechanical properties
MOHANTY A K, MISRA M, HINRICHSEN G. Biofibres, biodegradable polymers and biocomposites: An overview [J]. Macromolecular materials and Engineering, 2000, 276-277(1): 1-24.
ALADEJANA J T, WU Z, FAN M Z, et al. Key advances in development of straw fibre bio-composite boards: An overview [J]. Materials Research Express, 2020, 7(1): 012005.
李萍, 左迎峰, 吴义强, 等. 秸秆人造板制造及应用研究进展[J]. 材料导报, 2019, 33(15): 2624-2630.
LI P, ZUO Y F, WU Y Q, et al. Research progress on the manufacture and application of straw-based panel[J]. Materials Review, 2019, 33(15): 2624-2630.
刘广成. 玉米秸秆制作碎料板的可行性探讨[J]. 中国人造板, 2015, 22(5): 17-20.
LIU G C. Practicality of corn straw-based panel manufacturing[J]. China Wood-Based Panels, 2015, 22(5): 17-20.
左迎峰, 吴义强, 吕建雄, 等. 工艺参数对无机胶黏剂稻草板性能的影响[J]. 林业科技开发, 2016, 1(4): 25-32.
ZUO Y F, WU Y Q, LYU J X, et al. Effect of process parameters on the properties of rice straw board with inorganic adhesive[J]. China Forestry Science and Technology, 2016, 1(4): 25-32.
LI X J, CAI Z Y, Winandy J E, et al. Selected properties of particleboard panels manufactured from rice straws of different geometries[J]. Bioresource Technology, 2010, 101(12): 4662-4666.
郑超, 张雅云, 肖建平, 等. 刨花形态对麦秸板物理力学性能的影响[J]. 西北农林科技大学学报(自然科学版), 2015, 43(3): 191-198.
ZHENG C, ZHANG Y Y, XIAO J P, et al. Effect of particle geometry on physical and mechanical properties of wheat straw board[J]. Journal of Northwest A&F University (Natural Science Edition), 2015, 43(3): 191-198.
易顺民, 郝健, 晏晖, 等. 改性异氰酸酯施胶量及密度对麦秸刨花板性能的影响 [J]. 西南林业大学学报, 2013, 33(4): 94-97, 106.
YI S M, HAO J, YAN H, et al. Effect of modified isocyanate resin content and density on properties of wheat straw particleboard[J]. Journal of Southwest Forestry University, 2013, 33(4): 94-97, 106.
杨中平, 杨林青, 郭康权, 等. 玉米秸外皮碎料板制板工艺的初步研究[J]. 西北林学院学报, 1995: 67-72.
YANG Z P, YANG L Q, GUO K Q, et al. A preliminary study on the technologyof making cornstalk cuticles particleboard[J]. Journal of Northwest Forestry College, 1995: 67-72.
王琪, 胡晓丽, 李松, 等. 刨花形态对秸秆板材性能的影响试验研究[J]. 中国农机化, 2011, 32(3): 122-124.
WANG Q, HU X L, LI S, et al. Studies on influence of shaving shape of cornstalk particle on the physical and mechanical properties of cornstalk particleboard[J]. Chinese Agricultural Mechanization, 2011, 32(3): 122-124.
Badejo S O O. Effect of flake geometry on properties of cement-bonded particleboard from mixed tropical hardwoods[J]. Wood Science and Technology, 1988, 22(4): 357-369.
MEDVED S, GRUDNIK J. Influence of resin content on the surface covered with adhesive [J]. International Journal of Adhesion and Adhesives, 2021, 104: 102698.
张红杰, 张显权, 卢杰. 改性脲醛树脂胶玉米秸秆皮碎料板的制备工艺[J]. 东北林业大学学报, 2012, 40(6): 99-101.
ZHANG H J, ZHANG X Q, LU J. Preparation technology of corn stalk bark particle board with improved UF resin[J]. Journal of Northeast Forestry University, 2012, 40(6): 99-101.
张显权, 陆仁书, 王缘棣. 主要工艺参数对酚醛胶杨木刨花板尺寸稳定性的影响[J]. 东北林业大学学报, 2001, 29(5): 28-30.
ZHANG X Q, LU R S, WANG Y D. The effects of main technical parameters on dimensional stability of poplar particleboard boned with PF resin[J]. Journal of Northeast Forestry University, 2001, 29(5): 28-30.
顾继友, 高振华, 谭海彦. 制造工艺因素对刨花板吸水厚度膨胀率的影响[J]. 林业科学, 2003, 39(1): 132-139.
GU J Y, GAO Z H, TAN H Y. The effects of all main manufacturing factors on the thickness swelling in particleboard[J]. Scientia Silvae Sinicae, 2003, 39(1): 132-139.
吕建雄, 彭辉, 曹金珍, 等. 动态力学分析技术在木材科学研究领域的应用 [J]. 林业工程学报, 2018, 3(5): 1-11.
LYU J X, PENG H, CAO J Z, et al. Application of dynamic mechanical analysis in wood science research [J]. Journal of Forestry Engineering, 2018, 3(5): 1-11.
王辉, 杜官本, 岳秀, 等. 脲醛树脂胶接耐久性评价[J]. 粘接, 2015, 36(9): 56-58, 51.
WANG H, DU G B, YUE X, et al. Evaluation of urea-formaldehyde resin bonding durability[J]. Adhesion, 2015, 36(9): 56-58, 51.
田秀娟, 魏文阁, 张强, 等. 热分析技术在热固性树脂研究中的应用[J]. 山东化工, 2019, 48(11): 12-13, 15.
TIAN X J, WEI W G, ZHANG Q, et al. Application of thermal analysis technique in the study of thermosetting resins[J]. Shandong Chemical Industry, 2019, 48(11): 12-13, 15.
相关作者
相关机构
京公网安备11010802024621
微信公众号