Analysis of Optimization Manufacturing Technology of Poplar Plywood Glued with High Density Polyethylene Film

FANG Lu; CHANG Liang; GUO Wen-jing; WANG Zheng

doi:10.19455/j.mcgy.2013.05.005

Research & Development | Views : 0 下载量: 164 CSCD: 13

PDF
Export
Share
Collection
Album

Analysis of Optimization Manufacturing Technology of Poplar Plywood Glued with High Density Polyethylene Film
1. Key Laboratory of Wood Science and Technology of State Forestry Administration
2. Research Institute of Wood Industry,Chinese Academy of Forestry
Vol. 27, Issue 5, Pages: 17-20(2013)
DOI： 10.19455/j.mcgy.2013.05.005

扫描看全文

[1]方露,常亮,郭文静,王正.高密度聚乙烯膜制备杨木胶合板的工艺优化分析[J].木材工业,2013,27(05):17-20.

FANG Lu, CHANG Liang, GUO Wen-jing, et al. Analysis of Optimization Manufacturing Technology of Poplar Plywood Glued with High Density Polyethylene Film. [J]. China Wood Industry 27(5):17-20(2013)
[1]方露,常亮,郭文静,王正.高密度聚乙烯膜制备杨木胶合板的工艺优化分析[J].木材工业,2013,27(05):17-20. DOI： 10.19455/j.mcgy.2013.05.005.

FANG Lu, CHANG Liang, GUO Wen-jing, et al. Analysis of Optimization Manufacturing Technology of Poplar Plywood Glued with High Density Polyethylene Film. [J]. China Wood Industry 27(5):17-20(2013) DOI： 10.19455/j.mcgy.2013.05.005.

摘要

以高密度聚乙烯薄膜为胶黏剂制备无甲醛杨木胶合板,采用响应面方法优化胶合板的制备工艺。结果表明:热压温度、热压时间、薄膜用量对胶合板的胶合强度均有显著影响,热压温度和时间对胶合强度的交互影响显著。在优化工艺条件下制备的胶合板,胶合强度达1.68MPa,满足标准GB/T 9846.3-2004中II类胶合板的使用要求。

Abstract

High density polyethylene（HDPE） film was used as adhesive to make formaldehyde-free Poplar plywood.Response Surface Methodology（RSM） was used to optimize the processing technology for the plywood.The authors found that the bonding strength of the plywood was affected greatly by pressing temperature,pressing time as well as the film usage.The interaction effects between the pressing temperature and time were significant.The plywood bonding strength could reach 1.68 MPa under the optimum processing conditions as following:152 ℃ of pressing temperature,1.1 mm/min of pressing time,264.92 g/m2 of film usage,and could meet the requirement for type II plywood according to the National Standard of GB/T 9846.3-2004.

关键词

杨木胶合板木塑复合胶合板高密度聚乙烯薄膜响应面法胶合强度

Keywords

poplar plywoodwood-plastic plywoodhigh density polyethylene（HDPE） filmResponse Surface Methodology（RSM）bonding strength

references

Alert me when the article has been cited

提交

Studies on Low Toxicity,Nondewatering UF Resins Used for Poplar Plywood

Study on Corn Cob Modified by Calcium Carbonate Microcrystals and Its Preparation as Adhesive Filler for Urea-Formaldehyde Resin Adhesive

Manufacturing Process and Properties of Chlorella Protein-Based Adhesive

Toughening and Low Temperature Rapid Curing Modification of Phenol Formaldehyde Resin

Cold-pressing Technology for Making Parquet Substrates with Built-in Electric Heating Elements

相关机构

Research Institute of Wood Industry,CAF,Beijing 100091)

College of Materials Science and Engineering，Nanjing Forestry University

Guangxi Sanwei Forest Products Industry Co. LTD

College of Resources Environment and Materials，Guangxi University

College of Materials Science and Engineering，Northeast Forestry University

Address：Box 29，Research Institute of Wood Industry, No. 1, Dongxiaofu, Haidian District, Beijing Postal code：100091
Tel：010-62889419 Email：mckx@caf.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09064830号-19 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：16680

⁰