彭晓瑞,张占宽.塑膜增强柔性装饰薄木制备与饰面应用进展[J].木材科学与技术,2022,36(04):1-5.
PENG Xiao-rui,ZHANG Zhan-kuan.Preparation and Application of Plastic Film Reinforced Pliable Decorative Veneer[J].Chinese Journal of Wood Science and Technology,2022,36(04):1-5.
为了提高珍贵树种木材利用率和增加木制品附加值，塑膜增强柔性装饰薄木应运而生，产品具有很强的应用价值和广阔的市场前景。总结“十三五”期间新型塑膜增强柔性薄木制备工艺的研究进展，阐明不同种类塑膜增强柔性装饰薄木的可行性及适用性，分析塑膜增强柔性装饰薄木饰面应用的产业化优势和亟待解决的技术问题，并对其技术与应用发展趋势进行展望。
In order to improve the utilization rate of precious wood species and increase the added value of wood products, plastic-film reinforced pliable decorative veneer (PRPDSV) has been developed. These products have strong application value and broad market prospects. This paper reviewed the preparation, application status, and research progress of new products developed during the 13,th, Five-Year Plan period. The feasibility and applicability of different kinds of PRPDSV was analyzed. The specific industrial application progress of PRPDSV was expounded. Both the industrial advantages and technical problems of plastic film reinforced flexible decorative veneer were summarized. The development trend of its technology and application was prospected.
塑膜柔性装饰薄木制备技术应用进展
plastic-filmpliable decorative veneerpreparation technologyapplication progress
张德文, 张占宽, 彭晓瑞. 无纺布增强装饰薄木的柔韧性研究[J]. 木材工业, 2014, 28(5): 41-43.
ZHANG D W, ZHANG Z K, PENG X R. Flexibility of non-woven fabric reinforced decorative veneers[J]. China Wood Industry, 2014, 28(5): 41-43.
李年存, 向琴, 杨灿明. 柔性人造装饰薄木制造工艺的研究[J]. 中南林学院学报, 2000, 20(2): 40-43.
LI N C, XIANG Q, YANG C M. Study of the process of making soft artificial decorative veneer[J]. Journal of Central South Forestry University, 2000, 20(2): 40-43.
曾志高. 柔性装饰薄木制造工艺及应用技术研究[D]. 南京: 南京林业大学, 2003.
张占宽, 彭晓瑞, 张德文. 一种柔性复合薄木及其加工方法: CN103753656A[P]. 2014-04-30.
彭晓瑞, 张占宽. 一种无醛耐水塑膜增强柔性装饰薄木及其制备方法: CN106272804B[P]. 2018-08-10.
彭晓瑞, 张占宽. 柔性装饰薄木制备技术的现状及发展[J]. 木材工业, 2016, 30(6): 23-26.
PENG X R, ZHANG Z K. A review of manufacturing technology of flexible decorative veneers[J]. China Wood Industry, 2016, 30(6): 23-26.
赵敏. 塑料毒性与安全实用手册[M]. 北京: 化学工业出版社, 2004.
伞金福, 朱宝亮, 刘家浚, 等. 塑料表面改性对其摩擦学性能影响[J]. 摩擦学学报, 2000, 20(3): 236-240.
SAN J F, ZHU B L, LIU J J, et al. Effect of surface modification on tribological properties of plastics[J]. Tribology, 2000, 20(3): 236-240.
吴梦旦. 塑料薄膜与薄膜机械[J]. 轻工机械, 2000, 18(2): 4-6, 10.
WU M D. Plastic film and film machinery[J]. Light Industry Machinery, 2000, 18(2): 4-6, 10.
郭永翔. 用于塑料薄膜表面改性的水性涂料及其性能研究[D]. 广州: 华南理工大学, 2009.
赵允贵. 塑料薄膜行业发展形势分析[J]. 塑料包装, 2013, 23(5): 1-8.
ZHAO Y G. The analysis of plastic film industry development[J]. Plastics Packaging, 2013, 23(5): 1-8.
张宏艳, 程国君, 于秀华. 聚乙烯膜表面改性的研究现状[J]. 化工时刊, 2008, 22(8): 65-67.
ZHANG H Y, CHENG G J, YU X H. Current situation in surface modification of polyethylene membrane[J]. Chemical Industry Times, 2008, 22(8): 65-67.
桂祖桐. 聚乙烯树脂及其应用[M]. 北京: 化学工业出版社, 2002.
傅和青, 朱立红, 黄洪, 等. 聚丙烯薄膜特点及其在包装业的应用[J]. 包装工程, 2003, 24(5): 1-3.
FU H Q, ZHU L H, HUANG H, et al. Characteristics and applications of polypropylene film in packaging[J]. Packaging Engineering, 2003, 24(5): 1-3.
唐伟家. 流延聚丙烯薄膜[J].塑料加工应用, 2000, 22(3): 55-57.
李琼. 中国聚氯乙烯下游应用现状及发展趋势[J]. 中国氯碱, 2020(5): 1-4, 21.
LI Q. Application status and development trend of China PVC downstream[J]. China Chlor-Alkali, 2020(5): 1-4, 21.
权开玉. 聚氯乙烯行业的生产现状及发展趋势[J]. 橡塑技术与装备, 2018, 44(24): 32-39.
QUAN K Y. Production status and development trend of PVC industry[J]. China Rubber/Plastics Technology and Equipment, 2018, 44(24): 32-39.
袁东芝, 邓康清, 杨柱, 等. PET薄膜表面性能及其与紫外光固化涂层粘接性能相关性研究[J]. 化学与黏合, 2012, 34(4): 19-22, 40.
YUAN D Z, DENG K Q, YANG Z, et al. Research on the surface properties of PET films and their correlation to the adhesive properties of PET films/UV curing coatings[J]. Chemistry and Adhesion, 2012, 34(4): 19-22, 40.
刘方. 改性CA和PA膜的制备及性能研究[D]. 太原: 中北大学, 2016.
章蓉, 周晓燕, 汤丽娟, 等. 常压冷等离子体处理改善杨木单板胶合特性的研究[J]. 南京林业大学学报(自然科学版), 2013, 37(5): 169-171.
ZHANG R, ZHOU X Y, TANG L J, et al. Improvement bondability of poplar veneers by atmospheric pressure plasma discharge treatment[J]. Journal of Nanjing Forestry University (Natural Sciences Edition), 2013, 37(5): 169-171.
王洪艳, 杜官本, 韩永国, 等. DBD冷等离子体处理对云南松表面润湿性的影响[J]. 林业科技开发, 2013, 27(1): 35-37.
WANG H Y, DU G B, HAN Y G, et al. Influence of dielectric barrier discharge (DBD) cold plasma treatment on wettability of Pinus yunnanensis wood[J]. China Forestry Science and Technology, 2013, 27(1): 35-37.
周扬帆, 陈伊彬, 张涛, 等. 薄木贴面聚氯乙烯基木塑复合材料贴面工艺参数对其性能的影响[J]. 木材工业, 2020, 34(3): 10-13, 17.
ZHOU Y F, CHEN Y B, ZHANG T, et al. Effects of technical parameters on performance of veneered PVC-based wood/plastic composites[J]. China Wood Industry, 2020, 34(3): 10-13, 17.
Kim S, Kim H J. Comparison of standard methods and gas chromatography method in determination of formaldehyde emission from MDF bonded with formaldehyde-based resins[J]. Bioresource Technology, 2005, 96(13): 1457-1464.
CHEN W M, ZHOU X Y, ZHANG X T, et al. Fast enhancement on hydrophobicity of poplar wood surface using low-pressure dielectric barrier discharges (DBD) plasma[J]. Applied Surface Science, 2017, 407: 412-417.
PENG X R, ZHANG Z K. Plasma treatment of plastic film or decorative veneer and its effects on the peel strength and curling deformation of plastic film-reinforced pliable decorative sliced veneer (PR-RP-DSV)[J]. Holzforschung, 2019, 73(3): 313-322.
PENG X R, ZHANG Z K. Surface properties of different natural precious decorative veneers by plasma modification[J]. European Journal of Wood and Wood Products, 2019, 77(1): 125-137.
彭晓瑞, 张占宽. 等离子体改性提高塑膜增强柚木柔性薄木的胶合性能机理[J]. 东北林业大学学报, 2018, 46(6): 89-96.
PENG X R, ZHANG Z K. Reinforced mechanism of adhesion properties of polyethylene film enhanced teak decorative veneer by plasma modification[J]. Journal of Northeast Forestry University, 2018, 46(6): 89-96.
PENG X R, ZHANG Z K. Hot-pressing composite curling deformation characteristics of plastic film-reinforced pliable decorative sliced veneer[J]. Composites Science and Technology, 2018, 157: 40-47.
彭晓瑞, 张占宽. 凹凸模曲面热压成型制备塑膜增强薄木工艺优化[J]. 西北林学院学报, 2019, 34(6): 178-183, 223.
PENG X R, ZHANG Z K. Optimization of surface forming process of plastic film and decorative veneer by concave hot pressing[J]. Journal of Northwest Forestry University, 2019, 34(6): 178-183, 223.
彭晓瑞, 张占宽. 等离子体改性制备塑膜增强柔性装饰薄木工艺[J]. 木材工业, 2017, 31(3): 49-53.
PENG X R, ZHANG Z K. Manufacturing technology of flexible decorative veneers reinforced with low density polyethylene(LDPE) and treated by plasma[J]. China Wood Industry, 2017, 31(3): 49-53.
彭晓瑞, 张占宽, 杨旭. 制造工艺参数对聚乙烯膜增强柚木薄木性能的影响[J]. 木材工业, 2018, 32(3): 5-8.
PENG X R, ZHANG Z K, YANG X. Effects of manufacturing parameters on performance of teak decorative veneers enhanced with polyethylene films[J]. China Wood Industry, 2018, 32(3): 5-8.
彭晓瑞, 张占宽. 塑膜增强薄木贴面高密度纤维板的工艺优化[J]. 木材工业, 2017, 31(4): 39-42.
PENG X R, ZHANG Z K. Process optimization of high density fiberboard overlaid with veneer reinforced using low density polyethylene films[J]. China Wood Industry, 2017, 31(4): 39-42.
京公网安备11010802024621
微信公众号