汪为锴,李明晗,刘畅等.甲醇抽提处理对斜叶桉心材细胞壁孔隙结构特征的影响[J].木材科学与技术,2021,35(06):26-30.
WANG Wei-kai,LI Ming-han,LIU Chang,et al.Effect of Methanol Extraction on Cell Walls Pore Structure of Eucalyptus obliqua Heartwood[J].Chinese Journal of Wood Science and Technology,2021,35(06):26-30.
为研究斜叶桉心材细胞壁孔隙结构特征，利用甲醇对斜叶桉心材粉末进行抽提处理，再用气体吸附法和比重瓶法对甲醇抽提样和对照样进行细胞壁孔隙结构测试。在本试验条件下，通过比较两种试样的测试结果，发现斜叶桉心材抽提物主要存在于0.4~0.7 nm范围内细胞壁微孔中，抽提物的存在使斜叶桉心材细胞壁具有较小的孔体积和孔隙率，这可能是斜叶桉干燥速度慢的原因之一。
In order to investigate the effect of methanol extraction on cell walls pore structure of ,Eucalyptus obliqua ,heartwood, the heartwood powder was extracted with methanol. The cell wall pore structures of controlled and extracted samples were evaluated by the N,2, CO,2, sorption and pycnometer methods, respectively. The results indicated that ,Eucalyptus obliqua, heartwood extractives mainly existed in the micropores of cell walls in the range of 0.4~0.7 nm. The existence of extractives in the cell walls of ,Eucalyptus obliqua, heartwood led smaller pore volume and porosity, which possibly was one of the reasons for the slow drying speed of ,Eucalyptus obliqua, heartwood.
甲醇抽提斜叶桉心材细胞壁孔隙结构气体吸附法比重瓶法
methanol extractionEucalyptus obliqua heartwoodcell wall pore structuregas isotherm sorption methodpycnometer method
Redman A L, Bailleres H, Gilbert B P, et al. Finite element analysis of stress-related degrade during drying of Corymbia citriodora and Eucalyptus obliqua[J]. Wood Science and Technology, 2018, 52(1): 67-89.
Bootle K R. Wood in Australia. Types, properties and uses[M]. McGraw-Hill Book Company Sydney Australia, 1983.
YIN J P, SONG K L, LU Y, et al. Comparison of changes in micropores and mesopores in the wood cell walls of sapwood and heartwood[J]. Wood Science and Technology, 2015, 49(5): 987-1001.
Papadopoulos A N, Hill C A S. The sorption of water vapour by anhydride modified softwood[J]. Wood Science and Technology, 2003, 37(3-4): 221-231.
Östlund Å, Köhnke T, Nordstierna L, et al. NMR cryoporometry to study the fiber wall structure and the effect of drying[J]. Cellulose, 2010, 17(2): 321-328.
Borrega, Karenlampi, PP. Cell wall porosity in norway spruce wood as affected by high-temperature drying[J]. Wood Fiber Science, 2011,43(2):206-214.
Zauer M, Pfriem A, Wagenführ A. Toward improved understanding of the cell-wall density and porosity of wood determined by gas pycnometry[J]. Wood Science and Technology, 2013, 47(6): 1197-1211.
Chang S S, Quignard F, Alméras T, et al. Mesoporosity changes from cambium to mature tension wood: a new step toward the understanding of maturation stress generation in trees[J]. The New Phytologist, 2015, 205(3): 1277-1287.
Shi J, Avramidis S. Dried cell wall nanopore configuration of Douglas-fir, western red cedar and aspen heartwoods[J]. Wood Science and Technology, 2018, 52(4):1025-1037.
Stamm A . Wood and cellulose science[M]. Ronald Press Co, 1900.
Brunauer S, Emmett P H, Teller E. Adsorption of gases in multimolecular layers[J]. Journal of the American Chemical Society, 1938, 60(2): 309-319.
Barrett E P, Joyner L G, Halenda P P. The determination of pore volume and area distributions in porous substances I. computations from nitrogen isotherms[J]. Journal of the American Chemical Society, 1951, 73(1): 373-380.
Mulfort K, Farha O, Malliakas C, et al. An interpenetrated framework material with hysteretic CO2 uptake[J]. Chemistry-A European Journal, 2010, 16(1): 276-281.
苌姗姗, 胡进波, BrunoClair, 等. 氮气吸附法表征杨木应拉木的孔隙结构[J]. 林业科学, 2011, 47(10): 134-140.
CHANG S S, HU J B, BRUNO C, et al. Pore structure characterization of poplar tension wood by nitrogen adsorption-desorption method[J]. Scientia Silvae Sinicae, 2011, 47(10): 134-140.
Sing K S W. Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity (Recommendations 1984)[J]. Pure and Applied Chemistry, 1985, 57(4): 603-619.
Groen J C, Pérez-Ramı́rez J. Critical appraisal of mesopore characterization by adsorption analysis[J]. Applied Catalysis A: General, 2004, 268(1-2): 121-125.
相关文章
相关作者
相关机构
京公网安备11010802024621
微信公众号