Modification and Performance of Magnesium Oxychloride Adhesive for Plywood

WANG Ying; WANG Huishan; LYU Shaoyi; ZHANG Longfei; PENG Limin

doi:10.12326/j.2096-9694.2023149

RESEARCH PAPERS | Views : 0 下载量: 0 CSCD: 0 CNKI被引量: 0 Crossref: 0 Wos: 0 Scopus: 0 更多指标

PDF
Export
Share
Collection
Album

Modification and Performance of Magnesium Oxychloride Adhesive for Plywood
Research Institute of Wood Industry，Chinese Academy of Forestry，Beijing 100091，China
Vol. 38, Issue 4, Pages: 44-50(2024)
Published： 30 July 2024 ，
DOI： 10.12326/j.2096-9694.2023149
稿件说明：

移动端阅览

王颖,王慧珊,吕少一等.胶合板用氯氧镁胶黏剂的改性工艺与性能研究[J].木材科学与技术,2024,38(04):44-50.

WANG Ying,WANG Huishan,LYU Shaoyi,et al.Modification and Performance of Magnesium Oxychloride Adhesive for Plywood[J].Chinese Journal of Wood Science and Technology,2024,38(04):44-50.
王颖,王慧珊,吕少一等.胶合板用氯氧镁胶黏剂的改性工艺与性能研究[J].木材科学与技术,2024,38(04):44-50. DOI： 10.12326/j.2096-9694.2023149.

WANG Ying,WANG Huishan,LYU Shaoyi,et al.Modification and Performance of Magnesium Oxychloride Adhesive for Plywood[J].Chinese Journal of Wood Science and Technology,2024,38(04):44-50. DOI： 10.12326/j.2096-9694.2023149.

摘要

为了提高氯氧镁胶黏剂制备胶合板的胶合强度及耐水性能，采用磷酸和纳米二氧化硅作为改性剂，分析单一和复合添加改性剂后氯氧镁胶黏剂及其制备胶合板的各项性能。结果表明：磷酸和纳米二氧化硅的加入可以改善氯氧镁胶黏剂的物理力学性能，且两种改性剂在合适比例下复合添加的效果优于单一添加。当同时添加磷酸和纳米二氧化硅，两者添加量（以MgO质量计）分别为1%和3%时，改性氯氧镁胶黏剂的软化系数可达到0.95。傅立叶变换红外光谱仪、X射线衍射仪和扫描电子显微镜分析结果表明，两种改性剂并没有与氯氧镁胶黏剂发生化学反应，而是通过改变518相晶体的状态和纳米级颗粒填充孔隙，阻止518相晶体水解，抑制Mg（OH）

生成，使其具有更致密的结构。改性优化氯氧镁胶黏剂制备的胶合板的干、湿态胶合强度可达到1.51、1.25 MPa，满足GB/T 9846—2015《普通胶合板》≥0.70 MPa的要求。

Abstract

To improve the bonding strength and water resistance of plywood made with magnesium oxychloride adhesive

phosphoric acid and nano-silicon dioxide were used as modifiers. The properties of magnesium oxychloride adhesive and plywood prepared by adding single and composite modifiers were analyzed. The results show that the modification with phosphoric acid and nano-silica can improve the physical and mechanical properties of magnesium oxychloride adhesive. The effect of the composite of the two modifiers with an optimal proportion is better than that of either one single modifier. When phosphoric acid and nano-silica are added at the same time with a ratio of (calculated by MgO mass) 1% and 3% respectively

the softening coefficient of the modified magnesium oxychloride adhesive can reach 0.95. The analysis results from Fourier transform infrared spectrometer

X-ray diffractometer

and scanning electron microscope show t

hat the modifier does not chemically react with the magnesium oxychloride adhesive

but changes the state of 518 phase crystals and the filling of pores by nano-particles

which prevents the hydrolysis of 518 phase crystals

inhibits the generation of Mg(OH)

and forms a denser structure. The dry and wet bonding strengths of plywood prepared with optimal modified magnesium oxychloride adhesive can reach 1.51 and 1.25 MPa

which meets the requirement of ≥0.70 MPa of GB/T 9846—2015

Plywood for general use

关键词

氯氧镁胶黏剂磷酸纳米二氧化硅518相胶合强度耐水性能

Keywords

magnesium oxychloride adhesive (MOA)phosphoric acidnano silica518 phasesbond strengthwater resistance

references

王慧珊，吕少一，王颖，等. 胶合板用氯氧镁胶黏剂制备工艺的初步研究[J]. 木材科学与技术，2024，38(1): 66-72.

WANG H S, LYU S Y, WANG Y, et al. Preliminary study on preparation of magnesium oxychloride adhesive for plywood[J]. Chinese Journal of Wood Science and Technology, 2024, 38(1): 66-72.

WANG Y, WANG H S, ZHANG L F, et al. Optimization of raw-material ratios and curing temperature of magnesium oxychloride cement[J]. Construction and Building Materials, 2024, 435: 136795.

HUANG T J, YUAN Q, DENG D H. The role of phosphoric acid in improving the strength of magnesium oxychloride cement pastes with large molar ratios of H2O/MgCl2[J]. Cement and Concrete Composites, 2019, 97: 379-386.

LUO X R, FAN W Q, LI C Q, et al. Effect of hydroxyacetic acid on the water resistance of magnesium oxychloride cement[J]. Construction and Building Materials, 2020, 246: 118428.

CHITHRA S, SENTHIL KUMAR S R R, CHINNARAJU K. The effect of Colloidal Nano-silica on workability, mechanical and durability properties of High Performance Concrete with Copper slag as partial fine aggregate[J]. Construction and Building Materials, 2016, 113: 794-804.

ZHANG G, XIA H, NIU Y, et al. Microstructure refinement and affected zone reinforcement for internal curing cement paste by composite microgel with nano silica[J]. Cement and Concrete Composites, 2023, 138: 105013.

CHEN X, ZHANG T, BI W, et al. Effect of tartaric acid and phosphoric acid on the water resistance of magnesium oxychloride (MOC) cement[J]. Construction and Building Materials, 2019, 213: 528-536.

吴丹妮. 木材用镁质胶黏剂的制备与性能研究[D]. 北京: 北京林业大学, 2020.

曹锋, 乔宏霞, 李双营, 等. 生物质硅改性氯氧镁水泥复合材料的力学性能与作用机制[J]. 复合材料学报, 2023, 40(10): 5859-5870.

CAO F, QIAO H X, LI S Y, et al. Mechanical properties and mechanism of magnesium oxychloride cement composites modified by biomass silicon [J]. Journal of Composites:, 2023, 40(10): 5859-5870.

ZHOU W G, YE Q Q, SHI S Q, et al. A strong magnesium oxychloride cement wood adhesive via organic–inorganic hybrid[J]. Construction and Building Materials, 2021, 297: 123776.

王丰景. 氯氧镁水泥胶凝材料增强及耐水改性研究[D]. 合肥: 安徽大学, 2021.

TAN Y N, LIU Y, GROVER L. Effect of phosphoric acid on the properties of magnesium oxychloride cement as a biomaterial[J]. Cement and Concrete Research, 2014, 56: 69-74.

HU C L, XU B W, MA H Y, et al. Micromechanical investigation of magnesium oxychloride cement paste[J]. Construction and Building Materials, 2016, 105: 496-502.

Alert me when the article has been cited

提交

Preliminary Study on Preparation of Magnesium Oxychloride Adhesive for Plywood

Effect of Glue Spreading Methods on the Properties of Laminated Strand Lumber with Different Densities

Effect of Isocyanate Resin Content on Properties of High-Density Fiberboards

Effects of Hot-Pressing Temperature and Density on Properties of Cupressus funebris Scrimber

Preliminary Study on Improvement of Bond Strength of Low-Formaldehyde-Emission Urea-Formaldehyde Resin for Plywood